Epilox® Epoxy-amine adducts and blends
Below are the available Epilox® Epoxy-amine adducts and blends
Please click on the product names for the current data sheets
| Product name | Description
|
Amine equivalent weight (g) |
Viscosity at 25 °C (mPa·s) DIN 16 945 |
Colour (Gardner) DIN ISO 4630 |
Pot life to Tmax with Epilox®T 1938/700 (100 g, 23 °C) min / °C |
Applications |
| Epilox® hardener H 10-30 |
Modified cycloaliphatic amine adduct |
93 | 200 – 300 | max. 2 | 35 / 170 | Higher reactivity compared to Epilox® hardener H 10-33 |
| Epilox® hardener H 10-31 |
Modified cycloaliphatic amine adduct |
112 | 400 – 600 | max. 2 | 75 / 125 | General-purpose hardener, low yellowing tendency |
| Epilox® hardener H 10-32 |
Modified cycloaliphatic polyamine |
85 | 15 – 25 | max. 2 | 60 / 1701) | Low viscosity, high filler levels, nonylphenol-free coatings |
| Epilox® hardener H 10-33 |
Modified cycloaliphatic amine adduct |
93 | 80 – 120 | max. 2 | 65 / 150 | Mix ratio with Epilox® T 19-38/700 = 2 :1 (pbw resin : hardener) |
| Epilox® hardener H 10-34 |
Modified cycloaliphatic amine adduct |
93 | 70 – 120 | max. 1 | 50 / 180 | Low yellowing tendency |
| Epilox® hardener H 10-36 |
Modified cycloaliphatic polyamine |
85 | 40 – 60 | max. 2 | 30 / 1751) | Higher reactivity compared with Epilox® hardener H 10-32, nonylphenol-free coatings |
| Epilox® hardener H 10-41 |
Modified cycloaliphatic amine adduct |
93 | 70 – 120 | max. 2 | 65 / 140 | General-purpose hardener, nonylphenol-free coatings |
| Epilox® hardener H 10-69 |
Amine adduct | 46 | 20 – 40 | max. 3 | 25 / 1501)
30 / 1802) |
Special hardener for Epilox® M 1049, for chemical-resistant and nonylphenol-free coatings |
| Epilox® hardener M 989 |
Modified amine adduct | 63 | 200 – 300 | max. 2 | 70 / 160 | Nonylphenol-free coatings, mix ratio 3:1 with Epilox® T 19-38/700 (pbw resin : hardener) |
| Epilox® hardener M 1128 |
Modified amine adduct |
93 | 290 – 340 | max. 2 | 30 / 170 | Nonylphenol-free coatings, mix ratio 2:1 with Epilox® T19-38/700 (pbw resin : hardener) |
| Epilox® hardener M 1131-1 |
Modified amine adduct | 94 | 120 – 240 | max. 2 | 40 / 160 | Nonylphenol-free coatings, mix ratio 2:1 with Epilox® T 19-38/700 (pbw resin : hardener) |
| Epilox® hardener M 1142 |
Modified amine adduct | 85 | 40 – 80 | max. 2 | 45 / 1901) | Alkylphenol-free coatings, mix ratio 2:1 with Epilox® T 19-34/700 (pbw resin : hardener) |
| Epilox® hardener M 1148 |
Modified amine adduct | 100 | 150 – 230 | max. 2 | 145 / 70 | Hardener is used as curing agent for casting and laminating resin systems as well as for adhesives, low yellowing tendency. |
| Epilox® hardener M 1150 |
Modified amine adduct | 115 | 350 – 450 | max. 2 | 65 / 120 | General-purpose hardener, nonylphenol-free coatings |
| Epilox® hardener M 1164 |
Modified amine adduct | 93 | 170 – 270 | max. 2 | 65 / 165 | General-purpose hardener, nonylphenol-free coatings with good early water spot resistance, mix ratio 2:1 with Epilox® T 19-38/700 (pbw resin : hardener) |
| Epilox® hardener M 1167 |
Modified amine adduct | 115 | 280 – 380 | max. 2 | 85 / 110 | Longer pot life, nonylphenol-free |
| Epilox® hardener M 1171 |
Modified amine adduct | 93 | 160 – 260 | max. 2 | 65 / 160 | General-purpose hardener, nonylphenol-free coatings |
| Epilox® hardener M 1178 |
Activated modified polyamine | 75 | 180 – 320 | max. 6 | 20 / 215 | Cold cure below 10°C, Co-hardener and accelerator, no GHS 08 labeling, VOC-free, nonylphenol free |
| Epilox® hardener M 1180 |
Modified amine adduct | 122 | 5000 – 7000 | max. 2 | 45 / 1551) | Nonylphenol-free, for excellent chemical resistance and good surfaces |
| Epilox® hardener M 1189 |
Modified amine adduct | 95 | 220 – 320 | max. 2 | 35 / 185 | Hardener suitable for use in applications such as solvent-free floor coatings, epoxy mortars or protective coatings |
1) With Epilox® T 19-34/700 (modified, low viscosity, difunct. Bisphenol A/F resin which is resistant to crystallization).
2) With Epilox® M 1049 (modified, solvent-free bisphenol F resin).